Butyl Rubber Gloves Test Results
BUTYL RUBBER GLOVES TEST RESULTS FOR STYLES: CP-7, CP-14, CP-14F, CP-25, IBA-35
Breakthrough times and permeation rates reported are the average of three test replicates.
ND = No breakthrough time in 8 hours
NA = Not Applicable
NT = Not Tested
All tests performed on Style CP-25 (heavyweight) except as indicated. All tests performed per ASTM F739-85 by TRI/Environmental, Inc. at ambient temperature for 8 hours. Tests were performed under laboratory conditions and do not represent actual usage conditions. TRI/Environmental makes no warranties or other guarantees concerning protection by these materials and assumes no liability for use of this material with the chemicals tested.
The user should determine the applicability of conditions when assessing suitability of the actual anticipated exposures.
Download a printable version of Butyl Rubber Gloves Test Results in PDF format.
| Chemical | BreakthroughTime (min.) | Permeation Rate (ug/cm2-min.) |
|---|---|---|
| 1, 3 Butadiene | 303 | 0.3 |
| Acetaldahyde | 4 | 2.1 |
| Acetic Acid (glacial) | ND | NA |
| Acetone | ND | NA |
| Acetonitrile | ND | NA |
| Ammonia | ND | NA |
| Ammonium Hydroxide | ND | NA |
| Ammonium Nitrate | ND | NA |
| Aniline | ND | NA |
| Butyl Acetate | 94 | 10 |
| p-tert-Butyl Toluene | 91 | >32 |
| Carbinol | ND | NA |
| Carbon Disulfide | <4 | >500 |
| Chlorine | 60 | >50 |
| Chloromethane | 176 | 0.9 |
| Cyclohexane | 4 | >23 |
| Cyclohexanol | ND | NA |
| Cyclohexanone | ND | NA |
| Dibutyl Phthalate | ND | NA |
| Diethylamine | 27 | >500 |
| Dimethylformamide | ND | NA |
| Dioxane | ND | NA |
| Divinyl Benzene | 54 | >64 |
| Ethanal | 4 | 2.1 |
| Ethanamine | ND | NA |
| Ethyl Acetate | 253 | 6567 |
| Ethyl Alcohol | ND | NA |
| Ethyl Aldehyde | 4 | 2.1 |
| Ethylamine | ND | NA |
| Ethylene Oxide | 173 | 3.53 |
| Fluohydric Acid | ND | NA |
| Hexane | 21 | 86 |
| Hydrochloric Acid (37%) | ND | NA |
| Hydrofluoric Acid (49%) | ND | NA |
| Hydrogen Chloride | ND | NA |
| Hydrogen Fluoride (99%) | 15 | >100 |
| Methyl Alcohol | ND | NA |
| Methyl Chloride | 176 | 0.9 |
METHYL ETHYL KETONE (MEK) 99%
| Chemical | BreakthroughTime (min.) | Permeation Rate (ug/cm2-min.) |
|---|---|---|
| Style# CP-25 Heavy | 385 | 1.3 |
| Style# CP-14 Medium | 116 | 55 |
METHYL ISOBUTYL KETONE (MIBK) 99.5%
| Chemical | BreakthroughTime (min.) | Permeation Rate (ug/cm2-min.) |
|---|---|---|
| Style# CP-25 Heavy | 385 | 1.3 |
| Style# CP-7 Light | 68 | 7.6 |
| Methylene Chloride | 20 | >500 |
| Muriatic Acid (37%) | ND | NA |
| N-ethylethanamine | 27 | >500 |
| Nitric Acid (conc.) | ND | NA |
| Nitrobenzene | ND | NA |
| Nitropropane | ND | NA |
| N-hexane | 4 | >500 |
| Oleum | 270 | >500 |
| Phenylamine | ND | NA |
| Phosphoric Acid (conc.) | ND | NA |
| Potassium Hydroxide (50%) | ND | NA |
| Propyl Acetate | 109 | 19 |
| Sodium Hydroxide (50%) | ND | NA |
| Sulfuric Acid (conc.) | ND | NA |
| Sulfuric Acid (fuming) | 270 | >500 |
| Tetrachloroethylene | <4 | >500 |
| Tetrahydrofuran | 25 | >500 |
| Toluene | 28 | >500 |
| Toluene Diisocyanate | ND | NA |
| Vinylethylene | 303 | 0.3 |